<div dir="ltr"><div><div class="gmail_signature" data-smartmail="gmail_signature"><div dir="ltr">Cold rolled steel has a higher yield strength than hot rolled. For steel plate from the mill, that difference is significant. I do not know how much weaker the hot rolled rings would be than cold, or if it matters. </div><div dir="ltr"><br></div><div dir="ltr">I'm pretty sure the ABS design calculations don't take this additional strength into account. It's my understanding that in experimental tests those formulae tend to give rather conservative estimates of collapse depth, which is on purpose. Sean might be able to tell you in more detail.</div><div dir="ltr"><br></div><div dir="ltr"><div><br></div><div dir="ltr">-River J. Dolfi<div><br></div></div></div></div></div>