<p dir="ltr">Brian,<br>
7010 is a good choice  if you choose to do a smaw (stick ) root pass . I would refrain from using 6010 because of its lower tensile strength especially if  you are welding 516 gr 70. Have you considered TIG welding your root passes ? 70s filler wire would be best in that case. <br>

Dan Lance</p>
<div class="gmail_quote">On May 4, 2014 1:35 AM, "Brian Cox via Personal_Submersibles" <<a href="mailto:personal_submersibles@psubs.org">personal_submersibles@psubs.org</a>> wrote:<br type="attribution"><blockquote class="gmail_quote" style="margin:0 0 0 .8ex;border-left:1px #ccc solid;padding-left:1ex">
<div style="font-family:Arial,sans-serif;font-size:10pt"><div>I was wondering if anybody would know if there would be any significant difference in using 8010 rod as apposed to 6010 rod for the root pass when welding an end cap. </div>
<div> </div><div>Brian</div></div>
<br>_______________________________________________<br>
Personal_Submersibles mailing list<br>
<a href="mailto:Personal_Submersibles@psubs.org">Personal_Submersibles@psubs.org</a><br>
<a href="http://www.psubs.org/mailman/listinfo.cgi/personal_submersibles" target="_blank">http://www.psubs.org/mailman/listinfo.cgi/personal_submersibles</a><br>
<br></blockquote></div>